Mat.No. 1.2762, DIN 75CrMoNiW6-7

Short Description:

Designation by Standards Mat. No. DIN EN AISI 1.2762 75CrMoNiW6-7 - - Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.75 0.23 0.25 1.50 0.70 0.50 - 0.30 - Description Low alloyed cold working tool steel. Applications For high pressures. Heavy-duty tools for cold forging like dies, plates, punches, stamps Physical properties (avarage values) at ambient temperature Modulus of elasticity [103 x N/mm2]: 210 Density [g/cm3]: 7.88 ...

FOB Price: US $0.5 - 9,999 / Piece

Min.Order Quantity: 100 Piece/Pieces

Supply Ability: 10000 Piece/Pieces per Month

Port: Shenzhen

Payment Terms: L/C,D/A,D/P,T/T

Send email to us Download as PDF

Product Detail

FAQ

Product Tags

Designation by Standards

Mat. No.	DIN	EN	AISI
1.2762	75CrMoNiW6-7	-	-

Chemical Composition (in weight %)

C	Si	Mn	Cr	Mo	Ni	V	W	Others
0.75	0.23	0.25	1.50	0.70	0.50	-	0.30	-

Description
Low alloyed cold working tool steel.

Applications
For high pressures. Heavy-duty tools for cold forging like dies, plates, punches, stamps

Physical properties (avarage values) at ambient temperature
Modulus of elasticity [10³ x N/mm²]: 210
Density [g/cm³]: 7.88

Continuous Cooling Transformation (CCT) Diagram

Time-Temperature Transformation (TTT) Diagram

Soft Annealing
Heat to 710-750^oC, cool slowly. This will produce a maximum Brinell hardness of 210.

Hardening
Harden from a temperature of 870-900^oC followed by oil quenching. Hardness after quenching is 63 HRC.

Tempering
Tempering temperature: 130-300^oC.

Forging
Hot forming temperature: 1050-850^oC.

Machinability
No data.

Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.