Mat.No. 1.2064, DIN 85CrMo7

Short Description:

Designation by Standards Mat. No. DIN EN AISI 1.2064 85CrMo7 - - Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.85 0.25 0.30 1.75 - - - - - Description Low alloyed cold working tool steel. Applications Cold working steel parts and rolls for cold rolling. Physical properties (avarage values) at ambient temperature Modulus of elasticity [103 x N/mm2]: 210 Density [g/cm3]: 7.80 Soft Annealing Please ask. Normalizing Normalizing...

FOB Price: US $0.5 - 9,999 / Piece

Min.Order Quantity: 100 Piece/Pieces

Supply Ability: 10000 Piece/Pieces per Month

Port: Shenzhen

Payment Terms: L/C,D/A,D/P,T/T

Send email to us Download as PDF

Product Detail

FAQ

Product Tags

Designation by Standards

Mat. No.	DIN	EN	AISI
1.2064	85CrMo7	-	-

Chemical Composition (in weight %)

C	Si	Mn	Cr	Mo	Ni	V	W	Others
0.85	0.25	0.30	1.75	-	-	-	-	-

Description
Low alloyed cold working tool steel.

Applications
Cold working steel parts and rolls for cold rolling.

Physical properties (avarage values) at ambient temperature
Modulus of elasticity [10³ x N/mm²]: 210
Density [g/cm³]: 7.80

Soft Annealing
Please ask.

Normalizing
Normalizing temperature: Please ask.

Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650^oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

Hardening
Please ask.

Tempering
Tempering temperature: Please ask.

Forging
Hot forming temperature: 1050-850^oC.

Machinability
No data.

Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.