DIN 16MnCr5
Short Description:
Designation by Standards Brand Name Ravne No. Mat. No. DIN EN AISI ZF6 774 - 16MnCr5 - Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.16 max. 0.40 1.15 0.95 max. 0.08 max. 0.30 - - max.Al=0.035, max.Cu=0.30 DescriptionSpecial structural steel. ApplicationsHigher stressed components for automobile industry – gears, shafts, crankshafts, connecting rods, cam shafts, etc. Physical properties (avarage values) at ambient temperatureModulus of elasticity...
Product Detail
FAQ
Product Tags
Designation by Standards
| Brand Name | Ravne No. | Mat. No. | DIN | EN | AISI |
| ZF6 | 774 | - | 16MnCr5 | - |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 0.16 | max. 0.40 | 1.15 | 0.95 | max. 0.08 | max. 0.30 | - | - | max.Al=0.035, max.Cu=0.30 |
Description
Special structural steel.
Applications
Higher stressed components for automobile industry – gears, shafts, crankshafts, connecting rods, cam shafts, etc.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Soft Annealing
Please ask.
Normalizing
Please ask.
Hardening
Please ask.
Tempering
Please ask.
Forging
Hot forming temperature: 1050-850oC.
Machinability
Machining is best done with this alloy in the annealed or normalized and tempered condition. It can be machined by all conventional methods.
Forms manufactured: Please see the Dimensional Sales Program.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.