Mat.No. 1.2562, DIN 142W13

Short Description:

Designation by Standards Mat. No. DIN EN AISI 1.2562 142W13 - - Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 1.43 0.23 0.30 0.35 - - 0.25 3.05 - Description Low alloyed W cold working tool steel. Applications Cutting tools, stamping, woodworking, drawing, deep drawing and pressing tools, cold working rolls, measuring tools. Physical properties (avarage values) at ambient temperature Modulus of elasticity [103 x N/mm2]: 210 D...

FOB Price: US $0.5 - 9,999 / Piece

Min.Order Quantity: 100 Piece/Pieces

Supply Ability: 10000 Piece/Pieces per Month

Port: Shenzhen

Payment Terms: L/C,D/A,D/P,T/T

Send email to us Download as PDF

Product Detail

FAQ

Product Tags

Designation by Standards

Mat. No.	DIN	EN	AISI
1.2562	142W13	-	-

Chemical Composition (in weight %)

C	Si	Mn	Cr	Mo	Ni	V	W	Others
1.43	0.23	0.30	0.35	-	-	0.25	3.05	-

Description
Low alloyed W cold working tool steel.

Applications
Cutting tools, stamping, woodworking, drawing, deep drawing and pressing tools, cold working rolls, measuring tools.

Physical properties (avarage values) at ambient temperature
Modulus of elasticity [10³ x N/mm²]: 210
Density [g/cm³]: 8.0

Soft Annealing
Heat to 720-750^oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 270.

Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650^oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

Hardening
Harden from a temperature of 800-830^oC followed by water quenching. Hardness after quenching is 66 HRC.

Tempering
Tempering temperature: 100-250^oC.

Tempering Temperature (^oC) vs. Hardness (HRC)

100^oC	150^oC	200^oC	250^oC	300^oC
66	65	64	62	60

Tempering Diagram

Forging
Hot forming temperature: 1050-850^oC.

Machinability
No data.

Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.